Beverage containers coated with a water based liner

ABSTRACT

Water-based coating compositions for use as internal sanitary liners for metal containers containing beer, carbonated and noncarbonated soft drinks, and fruit juices consist essentially of aqueous dispersions of amine-solubilized interpolymers, said interpolymers being formed from substituted carboxylic acid amide units; ethylenically unsaturated acid units; hardening units from monomers such as styrene, vinyl toluene or alkyl methacrylates having from 1 to 4 carbon atoms and flexibilizing units from certain alkyl acrylates or methacrylates. The interpolymers are solubilized by neutralizing the acid units of the interpolymer with monomeric amines. In order to produce a stable composition, the amount of amine utilized in neutralizing the acid groups of the interpolymer should be sufficient to produce at least 0.200 milliequivalents of salt per gram of resin solids. These compositions provide containers with cured liners which do not impart undesirable turbidity or taste characteristics to the beer, soft drink, or fruit juices packaged therein.

CROSS REFERENCES TO RELATED APPLICATIONS

This application is a division of copending application Ser. No.494,688, filed Aug. 5, 1974, which in turn, now abandoned is acontinuation-in-part of copending application Ser. No. 470,480, filedMay 16, 1974.

BACKGROUND OF THE INVENTION

Beer, carbonated and non-carbonated soft drinks, and fruit juices(hereinafter referred to generically as beverages) are often packed incontainers made from aluminum, tin-free steel, blackplate or tinplate,which is cold rolled steel to which a thin layer of tin is applied. Manyof these beverages exert corrosive action upon the metal and in order toadequately protect the container and to prevent contamination of thepackaged material, a sanitary liner must be applied to the internalsurface of the container. However, the use of such liners also presentsseveral problems, one of the most troublesome being the residualturbidity and taste which tends to result from some liner materials.

Because of their relatively taste-free characteristics, vinyl polymersbased on vinyl chloride have been extensively employed in sanitaryliners in contact with beverages. While such vinyl polymers have beenuseful in the past, they possess a serious disadvantage which diminishestheir usefulness as sanitary liners at the present time. Thus, thesevinyl polymers are generally applied from volatile organic solventsolutions at relatively low solids contents and these solvent richsolutions either add to hydrocarbon air pollution or require expensivecontrol equipment.

In recent times, the increased emphasis on safety and environmentalpollution problems have resulted in a need for water-based compositionsfor such liners. By "water-based" it is meant compositions in solventscomprised predominantly of water, thus greatly reducing the handling andemissions of organic solvent vapors. However, the types of solvent-basedsanitary liners known and used heretofore are not obtainable assatisfactory water-based systems; indeed, it has been found thatwater-based materials as a class generally provide liners which impartundesirable turbidity and taste characteristics to beverages, even whenthe other necessary properties of such liners can be obtained.

The combination of properties which is necessary to successfulutilization of any composition for container liners, and which has notbeen satisfactorily obtainable in water-based sanitary liningcompositions known heretofore, includes the following:

A. PROPERTIES OF THE CURED LINER:

1. Metal Adhesion - Excellent adhesion to metals, including thealuminum, tin-free steel, blackplate and tinplate employed in beveragecontainers; this property permits the present compositions to beutilized either as a one-coat liner or as a primary and/or a topcoat ina two-coat system.

2. Taste Characteristics - Taste characteristics at least as good as thebest "tasteless" vinyl polymers applied from solvent solutions andutilized extensively in the container industry at the present time.

3. Turbidity Resistance - Beverages after packing, pasteurization andstorage must not develop undesirable turbidity and loss of appearance.

4. Fabricating Properties - Fabricating properties represent acombination of flexibility, extensibility and adhesion so as to permitforming operations to be carried out on the coated metal withoutcracking or otherwise impairing the continuity of the film.

5. Pasteurization Resistance - Beer is generally pasteurized at atemperature of 150° F. for 15 to 40 minutes; occasionally during thepasteurization temperatures as high as 160° F. to 180° F. may bereached.

6. Low Bake Properties - The curing or baking temperature in containersof the class described should not be excessively high because theexterior of some containers may be coated with lithographic coatings andinks which may discolor and lose their appearance at high temperatures.In addition, some containers employ adhesives as bonding agents and suchadhesives are adversely affected by high baking temperatures.

7. Extractability - No undesirable materials may be extracted from theliner during processing and storage.

8. Intercoat Adhesion - In order to permit use of primer or base coat,if desired, or added coats to repair defects, the liner compositionshould have good adhesion to itself and other conventionally utilizedmaterials.

B. PROPERTIES OF THE UNCURED COMPOSITION:

1. Application Properties - Application by equipment and methodsconventionally employed in the coatings industry. Thus, the compositionshould be capable of being applied by methods such as dipping, rollcoating, spraying and the like.

2. Storage Stability - The coating composition must be in a physicalform which permits handling and storage over varying conditions.Water-based compositions in emulsion form, for example, usually are notstorage-stable unless additives are employed which generally areundesirable in liners for containers used for comestible products.

Compositions containing amide interpolymers have been suggested for useon the exterior and, to some extent, on the interior of containers,e.g., see U.S. Pat. Nos. 2,870,117 and 3,117,693 and Canadian Pat. No.766,103. However, none of these patents describe a water-basedcomposition for use as a sanitary liner.

SUMMARY OF THE INVENTION

The present invention relates to a water-based coating composition foruse as an internal sanitary liner for metal containers adapted forpacking beverages, said composition consisting essentially of:

A. from about 5 percent to about 60 percent by weight of anamine-neutralized or partially-neutralized interpolymer formed in thepresence of a vinyl polymerization catalyst and in the absence ofmercaptan, said interpolymer being comprised of:

1. from about 5 percent to about 25 percent of acrylamide ormethacrylamide, the amide being reacted (before, during or afterpolymerization) with formaldehyde and alkanol to form units of thestructure: ##STR1## where R' is methyl or hydrogen and R is hydrogen orlower alkyl with at least 50 percent of the groups represented by Rbeing lower alkyl;

2. from about 3 percent to about 25 percent of units formed by vinylpolymerization of an ethylenically unsaturated carboxylic acid selectedfrom the group consisting of acrylic acid, methacrylic acid, itaconicacid, crotonic acid, and maleic acid and half esters of maleic andfumaric acid;

3. from about 5 percent to about 75 percent of units derived by vinylpolymerization of hardening monomer selected from the group consistingof styrene, vinyl toluene and alkyl methacrylates having from 1 to 4carbon atoms; and

4. from about 5 percent to about 75 percent of units formed by vinylpolymerization of flexibilizing monomer selected from the groupconsisting of alkyl methacrylates having up to 13 carbon atoms in eachalkyl group and alkyl methacrylates having 5 to 16 carbon atoms in eachalkyl group, wherein said interpolymer is solubilized by neutralizing orpartially neutralizing the acid groups of said interpolymer with asufficient amount of monomeric amine to produce at least 0.200milliequivalents of salt per gram of resin solids; and

B. from about 40 percent to about 95 percent by weight of a liquidmedium consisting of a mixture of a water-soluble or water-miscibleorganic solvent and water wherein at least 60 percent by weight of themixture is water.

The above compositions meet all the requirements for cured sanitaryliners set forth above. Thus, these compositions exhibit the followingproperties:

Metal adhesion - excellent adhesion to aluminum, tin-free steel,blackplate, tinplate, and other metals is obtained; no primer isnecessary.

Taste characteristics - extensive taste tests have confirmed that theseliners provide taste characteristics which make them acceptable to thebeverage industry.

Turbidity resistance - no turbidity is imparted to beverages andappearance after storage is unaffected.

Fabricating properties - metal coated with these compositions can beused in forming operations without rupturing or cracking the coating.

Pasteurization resistance - these coatings are not affected bytemperatures as high as 200° F., well above the temperature reachedduring pasteurization of beer.

Low bake properties - the coatings depending on their preciseformulation may be effectively cured at temperatures below 340° F., atemperature which is acceptable.

Extractability - in contrast to previous water-based coatings tested,these compositions do not release undesirable components. Testing of thepreferred systems show them to meet Food and Drug Administrationguidelines in this respect.

Intercoat adhesion - adhesion of successive coats and adhesion to othermaterials, such as epoxies, vinyls, polybutadiene, etc., issatisfactory.

It has also been found that the compositions of this invention can beapplied with existing equipment without the foaming problems normallyencountered in the application of previous water-based coatingcompositions. It has been further found that the compositions of theinvention can be prepared without employing additives such as mercaptanchain transfer agents, conventional surfactants and dispersionstabilizers and the like. This is an advantage in that it provides forcoating compositions having acceptable storage stability but which uponcuring provide films which are substantially free of additives which areundesirable in film compositions used for sanitary liners.

DETAILED DESCRIPTION OF THE INVENTION

In formulating a coating composition for use as an internal sanitaryliner for metal containers in which beverages are to be stored, it isextremely important that cured films produced from such coatingcompositions do not contain certain materials, even in residual amounts,which can be extracted by the beverage from the cured film. Thus, it hasbeen found that certain additives commonly employed in the preparationof prior art coating compositions may remain in residual amounts incured films produced from such compositions and that even residualamounts of such additives can adversely affect the characteristics ofbeverages in contact with such films. For example, residual amounts ofsuch materials as mercaptan chain transfer agents commonly employed inpolymerizing interpolymers such as those used and described herein;external surfactants or dispersion stabilizers; and externalcrosslinking agents such as amine-aldehyde resins in cured filmsemployed as sanitary liners for beverages such as beer have been foundto exert adverse effects on the turbidity and/or taste characteristicsof the beer. Accordingly, in formulating the compositions of thisinvention, such materials are avoided.

As indicated above, the term "beverage" as used throughout thespecification and claims refers to beer, carbonated and non-carbonatedsoft drinks, fruit juices, and the like.

Among the units in the interpolymers herein are units derived fromacrylamide or methacrylamide. These units may be formed from substitutedamides, such as N-(alkoxyalkyl)acrylamide or methacrylamide.N-(alkoxyalkyl)acrylamides or methacrylamides in which the alkoxy groupis butoxy (i.e., where R in the formula above is butyl) are especiallypreferred since interpolymers prepared from such substituted amidesexhibit the best balance of stability and efficient curing. In addition,mixtures of N-(alkoxyalkyl)acrylamide and N-methylolamide can also beused. These substituted amides can be prepared by several methods. Onepreferred method is to react an unsaturated amide (e.g., acrylamide)with formaldehyde and an alkanol (e.g., butanol) under acidic conditionsand in the presence of a polymerization inhibitor. For a detaileddescription of this method, see U.S. Pat. No. 3,079,434, incorporatedherein by reference. The resultant N-(alkoxyalkyl)acrylamide [e.g.,N-(butoxymethyl)acrylamide] is then interpolymerized with the othermonomers (described below) to form the interpolymer containing thesubstituted amide units.

As indicated, in the above method the substituted amide units of theinterpolymer herein are formed by first separately preparing thesubstituted amide and then interpolymerizing it with the other monomers.Alternatively, these substituted amide units can be formed in situ, thatis, the substituted amide units can be formed subsequent to theformation of the interpolymer. Thus, the unsaturated amide (e.g.,acrylamide or methacrylamide) can first be interpolymerized with theother monomers and the resultant product then reacted with the aldehyde(e.g., formaldehyde) and alkanol (e.g., butanol). For a more detaileddiscussion of this reaction, see U.S. Pat. No. 3,037,963, incorporatedherein by reference. This method has the disadvantage of requiringremoval of any excess formaldehyde which has a troublesome odor, and inthis method the degree of etherification of the methylol groups is moredifficult to control; thus, in the above structure, the proportion of Rgroups which are alkyl rather than hydrogen may not be as desired. Forgood stability at least 50 percent of these groups should be alkyl, andusually it is preferred that all or nearly all be alkyl.

As described above, the acrylamide or methacrylamide is in units ofpolymerized amide substituted with alkoxymethyl groups, with thealkoxymethyl substituent introduced either as part of the amide reactantor by reacting the polymerized amide with formaldehyde and alkanol. Ithas been the practice in the art to describe the proportion of amide inthese interpolymers by reference to the unsubstituted amide, e.g.,acrylamide or methacrylamide. This is because the alkoxymethyl groupsmay or may not be present in the monomer mixture used to form theinterpolymer, and if present may be of different molecular weightdepending on the particular group, and also because these groups splitoff and are substantially lost during the baking of the interpolymercoating. That practice is followed throughout the specification andclaims herein in referring to the proportion of amide. Thus, forexample, an interpolymer described as containing 10 percent acrylamidemay be formed from a monomer mixture containing 10 percent acrylamideitself (and the interpolymer later reacted with formaldehyde andalkanol), or the interpolymer may be formed from a monomer mixturecontaining N-(alkoxymethyl)acrylamide in an amount which would providean interpolymer containing 10 percent of the acrylamide moiety if thealkoxymethyl groups were removed. Where the latter is the case in theexamples, it is so indicated by stating the component as "Acrylamide asNBMA."

The interpolymer of the compositions of this invention contains fromabout 5 percent to about 25 percent of acrylamide or methacrylamide,with the preferred range being from about 10 percent to about 15percent.

For similar reasons, the levels of salt groups in thepartiallyneutralized interpolymers, as described in detail below, arecalculated herein based on interpolymers containing unsubstituted amide,i.e., not having alkoxymethyl substituents. The calculated valuescorrespond closely to experimental values based on the non-volatilesolids content of the interpolymer as obtained by heating at 150° C. for2 hours, thus simulating the losses incurred in the baking operationduring which alkoxymethyl groups are evolved.

The units of the interpolymer derived from ethylenically unsaturatedcarboxylic acid are best formed from acrylic acid or methacrylic acid,but itaconic acid, crotonic acid, and maleic acid, and half esters ofmaleic and fumaric acids may also be used. In the half esters, one ofthe carboxyl groups is esterified with an alcohol, the identity of whichis not significant so long as it does not prevent polymerization orpreclude the desired utilization of the product. Butyl hydrogen maleateand ethyl hydrogen fumarate are examples.

The interpolymer of the compositions of this invention may contain fromabout 3 to about 25 percent of such acid units. However, for the bestbalance of curing and ease of solubilization, it is preferred that theinterpolymer contain from 5 to 15 percent of the acid units. It shall benoted that interpolymers of the compositions in some instances containmore acid than is normally required for solubilization purposes. This isoften desirable in order to obtain satisfactory curing of theinterpolymer.

The other units in the interpolymer are derived from a combination ofhardening and flexibilizing monomers, to provide the desired combinationof properties. The hardening monomer is generally styrene, but otherssuch as vinyl toluene or alkyl methacrylates having from 1 to 4 carbonatoms can also be used.

The interpolymer of the compositions of this invention may contain fromabout 5 to about 75 percent of units derived from hardening monomerswith a preferred range being from about 40 to about 60 percent of suchunits.

The flexibilizing monomer component is one or more alkyl or substitutedalkyl esters of acrylic acid or methacrylic acid, the alkyl groupshaving 1 to 13 carbon atoms in the case of acrylic esters and 5 to 16carbon atoms in the case of methacrylic esters. Ethyl acrylate, butylacrylate, and 2-ethylhexyl acrylate, 2-ethylhexyl methacrylate, decylmethacrylate and lauryl methacrylate are examples. Ethyl acrylate isespecially preferred. The interpolymer of the compositions of thisinvention may contain from about 5 to about 75 percent of units derivedfrom flexibilizing monomers with a preferred range being from about 20to about 50 percent of such units.

The compositions of this invention may contain from about 5 percent toabout 60 percent by weight, preferably 15 to 40 percent by weight, ofthe interpolymer, the balance being the liquid medium.

The interpolymer is formed by polymerization in the presence of a vinylpolymerization catalyst. The preferred catalysts are azo compounds, suchas, for example, alpha, alpha'-azobis(isobutyronitrile). Other usefulcatalysts are tertiary-butyl perbenzoate, tertiary-butyl pivalate,isopropyl percarbonate and similar compounds. In some instances, otherfree radical catalysts such as benzoyl peroxide and cumene hydroperoxidemay also be useful.

As indicated above, the polymerization is carried out in the absence ofa mercaptan. This is an important consideration because it has been thepractice, as illustrated by the above patents, to employ small amounts(e.g., one percent to 3 percent) of a mercaptan as a chain transferagent in the preparation of amide interpolymers of this desired type. Ithas been found that the presence of even these small amounts ofmercaptan in the interpolymer composition results in compositions whichare unsuitable for use in sanitary liners for beer and similarbeverages. When a mercaptan is present, the lining imparts anundesirable taste characteristic to the beverage, especially on storagefor a period of several weeks. Since packed beverages are normallypacked for some period of time before they are used, this precludes theutilization of such interpolymer compositions as liners for thesecontainers.

The compositions of this invention are composed of dispersions of theabove-described interpolymers in a liquid medium. The liquid medium mayconsist entirely of water in some cases but, more commonly, will consistof a mixture containing a major proportion of water and a minorproportion of water-soluble or water-miscible organic solvents.

Suitable organic solvents are the ether type alcohols, such as ethyleneglycol monobutyl ether (ethyl Cellosolve) and the like, and loweralkanols having 2 to 4 carbon atoms such as ethanol, propanol,isopropanol, butanol, and the like. Minor proportions of hydrocarbonsolvents such as xylene, toluene, and the like may also be present inthe liquid medium. Mixtures of the ether type alcohols and loweralkanols can also be used. The preferred water-soluble, orwater-miscible organic solvents are mixtures of butyl Cellosolve andisopropyl alcohol. The liquid medium portion of the compositions of thisinvention may contain from about 60 percent to about 100 percent,preferably 80 percent, by weight of water and from about 0 percent toabout 40 percent, preferably 20 percent, by weight of water-soluble orwater-miscible organic solvent. In any event, the liquid medium willcontain at least 60 percent by weight of water. It should be noted thatwhile ordinary tap water can be used in the composition of thisinvention, deionized or distilled water is preferred. Based on totalweight of the composition, the composition may contain from about 40percent to about 95 percent, preferably 60 to 85 percent, by weight ofthe liquid medium.

The interpolymer herein is rendered water-reducible or dispersible bythe addition of a monomeric amine solubilizing agent. As is known in theart, acid group-containing interpolymers such as those employed in thepresent compositions can be rendered water-soluble or water-reducible byneutralizing or partially neutralizing the acid groups therein withamines. In general, the monomeric amines employed herein for thatpurpose may be any of the amines used for solubilizing resin systemsknown heretofore, including ammonia, ethyl amine, butylamine,dimethylamine, cyclohexylamine, morpholine, monoethanolamine,diethanolamine, diethylethanolamine, and the like. The preferred aminesherein are monoethanolamine and dimethylethanolamine withdimethylethanolamine being particularly preferred since it has beenfound to provide the best results. While, as indicated above, amines mayin general be used, there are certain considerations which should betaken into account in choosing the amine used to neutralize anyparticular system; for example, some amines are more effective thanothers in providing stable compositions, depending upon the degree ofneutralization of the interpolymer.

The term "degree of neutralization" refers to the amount of acid in theinterpolymer (as determined theoretically) which has been neutralizedwith amine. Thus, for example, if 20 percent of the theoretical amountof acid in the interpolymer has been neutralized with amine, the degreeof neutralization is 20 percent theoretical neutralization; if 30percent of the theoretical amount of acid has been neutralized, thedegree of neutralization is 30 percent theoretical neutralization, andso forth. In all cases, the degree of neutralization and the amount ofamine is sufficient to provide a stable composition, which is defined asone which does not separate into distinct phases, and retains itsapplication properties on storage. When it is desired that this beaccomplished at a relatively low degree of neutralization, i.e., belowabout 30 percent, the preferred amines, dimethylethanolamine andmonoethanolamine, should be used. At higher degrees of neutralization(i.e., 30 percent or above), other amines are effective. Thus, forexample, at 30 percent theoretical neutralization, diethylethanolamineproduces good results and at say 50 percent theoretical neutralization,essentially all of the above-listed amines are suitable.

The amount of amine employed in producing the water-based coatingcompositions of this invention is an important aspect of the invention.This amount is particularly significant at lower degrees ofneutralization of the interpolymer if a stable composition is to beobtained.

The amount of amine employed in producing the water-based coatingcomposition of this invention may in some cases be as low as an amountsufficient to produce 0.180 milliequivalent of salt per gram of resinssolids, but ordinarily will be an amount sufficient to produce at least0.200 milliequivalent of salt per gram of resin solids. The term "milliequivalents of salt per gram of resin solids" refers to the number ofacid milliequivalents per gram of resin solids of the interpolymer whichhave been neutralized with a base (i.e., an amine). The number ofmilliequivalents of salt per gram of resin solids can be determined bycalculation using the following formula: ##EQU1## wherein N is thedegree of neutralization. A degree of neutralization greater than 100percent indicates that excess base has been used. In this lattersituation, the value of 100 perent is used in the above calculation. Asindicated above, the compositions of this invention will ordinarilycontain at least 0.200 milliequivalents of salt per gram of resinsolids.

The upper limit in the amount of amine employed is somewhat lessimportant and is governed to a large degree by the method ofapplication. Thus, for example, if the composition is to be applied bybrushing, roll coating or dipping, the amine may be used in an amountwhich will produce as much as 3.47 milliequivalents of salt per gram ofresin solids. However, preferably, even in the above methods the amountof amine employed does not exceed an amount which will produce 1.910milliequivalents of salt per gram of resin solids. Moreover, when thecomposition is to be applied by spraying, the amount of amine employedordinarily should not produce more than 0.764 milliequivalents of saltper gram of resin solids although in some instances an amount of aminewhich will produce up to about 1.40 milliequivalents of salt per gram ofresin solids may be used.

The preferred method for producing water-based coating compositions ofthis invention comprises the steps of (a) polymerizing the substitutedamide, ethylenically-unsaturated acid, hardening and flexibilizinbmonomers in an escess of a mixture of water-soluble or water-miscibleorganic solvents, the solvent mixture consisting essentially of anethertype alcohol selected from the group consisting of ethyl Cellosolveand butyl Cellosolve and a lower alkanol selected from the groupconsisting of ethanol, propanol, isopropanol and butanol, wherein theexcess solvent in the mixture is essentially the lower alkanol, in thepresence of a polymerization catalyst to form the interpolymer insolution; (b) stripping off the excess solvent consisting essentially oflower alkanol by distillation at atmospheric pressure, under vacuum, orboth; (d) adding monomeric amine to the interpolymer solution; (d)adding water to the interpolymer solution under conditions of agitationto form a dispersion of the interpolymer; and (e) heat aging thedispersion at temperatures of from about 70° C. to about 90° C., whilemaintaining conditions of agitation until the viscosity of thedispersion is substantially constant.

The term "excess" as employed with reference to the organic solventmixture in step (a) above means that the total amount of organic solventmixture employed in the polymerization process exceeds the total amountof organic solvent desired in the final composition. The period of heataging, i.e. step (e), depends upon several factors, such as thecomposition of the interpolymer, the solids content of the composition,the initial viscosity of the interpolymer formed, the degree ofagitation and the like. In general, the heat aging period can range fromone hour or less up to about 11 hours.

In a particularly preferred embodiment of the above method, theabove-described monomers are polymerized in an excess of a solventmixture consisting essentially of butyl Cellosolve and isopropanol,wherein the excess solvent of the mixture is essentially isopropanol, inthe presence of an azo polymerization catalyst to form the interpolymerin solution. Then, the excess solvent consisting essentially ofisopropanol is stripped off by distillation at atmospheric pressure orunder vacuum, or both, following which the monomeric amine is added tothe interpolymer solution. Then deionized water at a temperature rangingfrom 50° C. to 99° C. (i.e., hot water) is added to the solution to forma dispersion of the interpolymer and finally the interpolymer dispersionis heat aged as in step (e) above.

The preferred embodiment of preparing the water-based coatingcompositions of this invention provides a number of significant andimportant advantages. First, the use of butyl Cellosolve and isopropanolas the solvent mixture provides a significant advantage because of thewide difference in the boiling points of these materials (i.e., butylCellosolve = 171.2° C., isopropanol = 82.4° C.). This difference isboiling points permits the ready removal (e.g., by distillation) ofisopropanol from the mixture. Accordingly, where as here, the excesssolvent (as defined above) employed in the polymerization procedure isessentially isopropanol, such excess is readily removable and the totalsolvent content of the final composition is more easily controlled.Secondly, the isopropanol in the solvent mixture functions as achain-transfer and molecular weight control agent in this system. Hence,in the preferred embodiment, isopropanol effectively controls themolecular weight of the interpolymer without the necessity of using anexternal or added chain transfer agent, such as the mercaptan chaintransfer agents normally employed in polymerizing interpolymers of thistype. Finally, the addition of hot water to the interpolymer solution isadvantageous in that it aids in the formation of the interpolymerdispersion and permits the more rapid attainment of coating compositionviscosity.

As indicated, the above-described methods are directed to thepreparation of the preferred water-based coating compositions in which aportion of the organic solvent originally employed in the polymerizationof the interpolymer remains in the final resin composition. However, asindicated previously in the specification, water-based coatingcompositions in which the liquid medium is entirely water are alsocontemplated as being within the scope of this invention. Suchcompositions may be obtained by following the above-described methodsand then employing an additional separation procedure following step(e). Thus, for example, the organic solvent remaining in the compositionafter step (e) can be removed by various separation procedures such asdistillation, liquid chromatography and the like.

The water-based coating compositions of this invention can be applied bymethods conventionally employed in the coatings industry, such asbrushing, dipping, roll coating, spraying, and the like and they areparticularly adapted to be applied by the methods used to coatcontainers. In this regard, it should be observed that the exactformulation of the coating composition employed herein (e.g., totalsolids, viscosity, etc.) will depend upon the desired manner in whichthe composition is to be applied. Thus, within the compositionallimitations set forth in the specification above, compositions havingsuitable application properties (e.g., solids contents, viscosity, etc.)can be readily selected for the the method of application desired. Sucha determination is well within the skill of those in the coating art.

After application, the compositions are ordinarily dried and cured bybaking at elevated temperatures to produce a hard, thermoset film. Thebaking schedules depend upon the nature of the particular composition,the nature of the substrate, and the manner in which it is to be used.In general, the water-based coating compositions of this invention canbe cured by using typical baking schedules employed in the containerindustry. Typical baking schedules for such container coatings employtemperatures ranging from about 300° F. to about 420° F. and timesranging from about 2 minutes to about 15 minutes.

The following examples are submitted to further illustrate the nature ofthe present invention and are not intended as a limitation on the scopethereof. All parts and percentages used in the examples and throughoutthe specification, are by weight unless otherwise indicated. The solidscontents reported in the examples were run at 105° C. as a qualitycontrol test.

EXAMPLE 1

This example illustrates the preparation of a water-based coatingcomposition of this invention.

Into a reactor equipped with reflux condenser, heating means, stirrer,thermometer and nitrogen feed liner were charged 159.0 grams of ethylCellosolve, 325.0 grams of isopropanol, and 290 grams of a monomermixture consisting of 5.9 percent glacial acrylic acid, 28.2 percent ofa 61.5 percent solids solution of N-(butoxymethyl)acrylamide (NBMA) in a1:3 solvent mixture of toluene and butanol, 32.1 percent of styrene,32.5 percent of ethyl acrylate and 1.3 percent alpha,alpha'-azobis(isobutyronitrile) catalyst (based on monomer solids, themonomer charge contains 10 percent acrylamide NBMA, 41 percent styrene,41.5 percent ethyl acrylate and 7.5 percent acrylic acid). The chargedmixture was then heated under nitrogen to reflux temperature (about 90°C-93° C.) in a period of about 45 minutes. After reflux had begin, anadditional 1081 grams of the above monomer mixture were added to thereactor over a period of about 3 hours. Then 12.0 grams of t-butylperbenzoate were added in 3 equal increments (i.e., 4 grams each) over aperiod of about 6 hours with each increment being added at two-hourintervals. At the end of the six-hour period, 337 grams of solvent(slightly more than the original amount of isopropanol used) werestripped from the resultant interpolymer solution by distillation atatmospheric pressure at a temperature of about 94° C. over a period ofabout 75 minutes. At this point, a sample of the reaction mixture wasanalyzed for total solids content and found to have a solids contentmeasured at 150° C. of 73 percent by weight. Then 49.8 grams (50 percenttheoretical neutralization) of dimethyl ethanolamine were added to thereaction mixture (temperature of the mixture about 97° C.). Afteraddition of the dimethyl ethanolamine was completed, 1939 grams ofdeionized water preheated to 75° C. was added to the reaction mixturewith stirring and the stirring was continued for about one hour afterthe addition of deionized water was completed.

The water-based coating composition resulting from the above procedureis a dispersion of interpolymer in a liquid medium, the composition hasthe following formulation:

    ______________________________________                                                          Interpolymer Units                                          Interpolymer      (Percent)                                                   Acrylamide as NBMA*                                                                             10.0                                                        Styrene           41.0                                                        Ethyl acrylate    41.5                                                        Glacial acrylic acid                                                                             7.5                                                        Liquid Medium     Percent by Weight                                           Deionized water   83.8                                                        Organic solvents**                                                                              16.2                                                        ______________________________________                                          *N-(butoxymethyl)acrylamide                                                   **A mixture consisting of ethyl Cellosolve, isopropanol, toluene and         butanol.                                                                 

The composition has the following properties:

    ______________________________________                                        Polymer solids:                                                                           33.4 percent by weight of total composition                       Liquid Medium:                                                                            65.6 percent by weight of total composition                       Viscosity:  140 centipoises, Brookfield viscosity                                         at 77° F., Spindle No. 4 at 20 r.p.m.                      Acid No.    16.1                                                              Milliequivalents                                                              of salt                                                                       per gram of                                                                   resin solids:                                                                             0.521                                                             Stability:  Good                                                              ______________________________________                                    

The composition was drawn down on a metal substrate and baked for twominutes at 375° F., producing a smooth, hard and durable film.

EXAMPLE 2

In this example, Example 1 was repeated except that the amount ofdimethyl ethanolamine used to neutralize the interpolymer was reduced by40 percent (to 30 percent theoretical neutralization) and the amount ofisopropanol increased by 10 percent to adjust the viscosity. Thefinished composition had the following properties:

    ______________________________________                                        Polymer solids:                                                                            35 percent by weight of total composition                        Liquid medium*:                                                                            65 percent by weight of total composition                        Viscosity    100 centipoises, Brookfield viscosity                                         at 77° F., No. 4 spindle at 20 r.p.m.                     Acid No.:    17.43                                                            Milliequivalents                                                              of salt                                                                       per gram of                                                                   resin solids:                                                                              0.314                                                            Stability:   Good                                                             ______________________________________                                          *85 percent by weight of deionized water and 15 percent by weight of         organic solvents.                                                        

The composition when drawn down on a metal substrate and baked for 2minutes at 375° F. produced a smooth, hard and durable film.

EXAMPLE 3

This example illustrates the preparation of a preferred water-basedcoating composition of the invention in which the ether-type alcoholemployed was butyl Cellosolve.

Into a reactor having the same equipment as in Example 1 were charged477 grams butyl Cellosolve, 975 grams of isopropanol and 870 grams ofthe monomer mixture of Example 1 with the alpha,alpha'-azobis(isobutyronitrile) catalyst removed. The charged mixturewas then heated under nitrogen to reflux employing the same conditionsas in Example 1. After the onset of reflux, an additional 3189 grams ofthe monomer mixture of Example 1 and 54 grams of alpha,alpha'-azobis(isobutyronitrile) catalyst were added to the reactor overa three-hour period as in Example 1. Following this addition, 12.0 gramsof t-butyl perbenzoate were added to the reactor using the additionprocedure of Example 1. Then 981 grams of organic solvent were removedby distillation at atmospheric pressure at temperatures ranging fromabout 95° C. to about 120° C. Subsequently, 89.4 grams (30 percenttheoretical neutralization) of dimethyl ethanolamine were added to thereaction mixture. After this addition, 5085 grams of deionized waterpreheated to 75° C. were added to the reaction mixture with stirring asin Example 1.

The resultant water-based coating composition has the followingformulation:

    ______________________________________                                                     Percent by weight total solids = 38.5                                         Interpolymer Units                                               Interpolymer (Percent)                                                        Acrylamide as NBMA                                                                         10.0                                                             Styrene      41.0                                                             Ethyl acrylate                                                                             41.5                                                             Glacial acrylic acid                                                                        7.5                                                                          Percent by weight total liquid = 61.5                            Liquid medium                                                                              Percent by weight                                                Deionized water                                                                            83.5                                                             Organic solvents*                                                                          16.5                                                             ______________________________________                                         *Consisting of butyl Cellosolve, isopropanol, toluene and butanol.       

The composition had the following properties:

    ______________________________________                                        Total solids:                                                                              38.5 percent                                                     Acid number: 17.7                                                             Viscosity:   300 centipoises, Brookfield viscosity at                                      77° F., No. 4 Spindle at 20 r.p.m.                        Milliequivalents                                                              of salt                                                                       per gram of                                                                   resin solids:                                                                              0.313                                                            Stability:   Good                                                             ______________________________________                                    

The composition when drawn down on a metal substrate and cured as in thepreceeding examples produced a smooth, hard and durable film.

EXAMPLE 4

In this example, a water-based coating composition was prepared inaccordance with the manner used in Example 3, except that additionalbutyl Cellosolve was employed to increase the organic solvent content ofthe composition. The composition had the following formulation:

    ______________________________________                                                            Total Weight                                              Interpolymer as in Example 3                                                                      37.5%                                                     Liquid medium       62.5%                                                                         Percent by Weight                                         Deionized water     79.5                                                      Organic Solvents    20.5                                                      ______________________________________                                    

The composition had the following properties:

    ______________________________________                                        Total solids:  37.5 percent                                                   Viscosity:     16.5 seconds, No. 4 Ford cup                                   Acid No.       18.6                                                           Milliequivalents                                                              of salt                                                                       per gram of                                                                   resin solids:  0.313                                                          Stability      Good                                                           ______________________________________                                    

The composition when applied to a metal substrate and cured as inExamples 1-3 produced a smooth, hard and durable film.

EXAMPLES 5-8

These examples illustrate the critical effect of the degree ofneutralization and thus the amount of salt produced per gram of resinsolids on the stability of the water-based coating compositions of thisinvention.

In this evaluation, compositions were prepared in substantially the samemanner and using the same interpolymer as in Examples 3-4 except thatthe amount of dimethyl ethanolamine employed was such that the degree ofneutralization of the interpolymer was 30 percent of theoreticalneutralization (hereafter TN) in Example 5, 25 percent TN in Example 6,20 percent TN in Example 7 and 15 percent TN in Example 8. Since thelower degrees of neutralization resulted in high composition viscosity(i.e., Examples 6-8), the solids content of these compositions werereduced by adding additional solvent in the form of an 80/20 mixture ofdeionized water and butyl Cellosolve. The resultant compositions had thefollowing formulations and properties:

    __________________________________________________________________________                       EXAMPLE                                                    __________________________________________________________________________                       5     6     7     8                                        __________________________________________________________________________    Interpolymer       ← (As in Example 4, above)→                    Percent theoretical neutralization                                                               30    25    20    15                                       Total solids (weight percent)                                                                    36.4  33.1  18.0  25                                       Total liquid medium (weight percent)                                                             63.6  66.9  82.0  75                                       Viscosity, No. 4 Ford cup, seconds                                            at 77° F.   26    31    25    --                                       Acid number        18.6  19.4  12.9  12.1                                     Milliequivalents of salt per gram                                             resin solids       0.312 0.261 0.208 0.156                                    Stability          Good  Good  Fair --                                                                             Bad --- Slight two phase                                                settling                                                                            separation                               __________________________________________________________________________

As can be seen from these examples, the stability of the compositiondepends upon the degree of neutralization and thus the amount of saltper gram of resin solids produced.

The above examples were repeated using monoethanolamine in place ofdimethyl ethanolamine and showed similar stability results.

EXAMPLE 9

This example illustrates a water-based coating composition of thisinvention having low temperature baking properties.

In this example, the composition was prepared in substantially the samemanner as in Examples 1-8 except that the monomer charge consisted of 10percent acrylamide as NBMA, 10 percent acrylic acid, 30 percent ethylacrylate and 50 percent styrene; the stripping procedure was carried outunder vacuum, and the degree of neutralization of the acid groups of theinterpolymer was 27 percent TN. The resultant composition had thefollowing formulation and properties:

    ______________________________________                                        Interpolymer                                                                  (composition                                                                  as above): 35 percent by weight                                               Liquid medium*:                                                                          65 percent by weight                                               Viscosity: 340 centipoises, Brookfield viscosity at                                      77° F., No. 4 spindle at 20 r.p.m.                          Acid number:                                                                             25.3                                                               Milliequivalents                                                              of salt                                                                       per gram of                                                                   resin solids:                                                                            0.375                                                              Stability  Good                                                                 *82.3 percent by weight of deionized water and 17.7 percent by weight of     organic solvents consisting of butyl Cellosolve, isopropanol, butanol and     xylene.                                                                  

The above composition when applied to a metal substrate can be cured in4 minutes at 320° F. to produce a smooth, hard and durable film.

As indicated above, the compositions of this invention are especiallyadapted for use as internal sanitary liners for beverage containers. Thefabrication of beverage containers (e.g., beer containers) and theapplication of sanitary liner compositions thereto are known in the art.The precise method of fabrication and internal sanitary linerapplication will vary depending on whether the beverage container ismade in two pieces or three pieces.

For example, one method of producing a two piece can involves firstforming a cup (e.g., by punch press) from metal sheet stock. The cup isthen drawn into a container (i.e., can) of the desired size and trimmed.Following the trimming operation, the can is then cleaned, printed andvarnish applied to the outside surface and bottom thereof. The can isthen baked to cure the outside varnish coating. Then the internalsanitary liner composition is applied to the inside of the container byspraying and the can is again baked to cure the sanitary liner.Subsequently, (i.e., after the can is packed) a can end which haspreviously been stamped from the metal sheet stock and coated withsanitary liner is applied to the can, generally by double seaming toseal the can. For a method of producing three piece cans, see U.S. Pat.No. 3,117,693.

As indicated at the beginning of the specification, the sanitary linerof such beverage containers are subjected to a number of tests. Thesetests are performed on the liner both prior to and after the containeris packed with beverages (e.g., beer). When such a container is packagedwith beer and sealed, the beer is subjected to pasteurization and othernormal processing operations. After the containers have been subjectedto storage, they are opened and both the beer and the liner areevaluated. The following are some of the more important tests which havebeen developed to measure the sanitary liner compositions for beveragecontainers:

a. metal adhesion;

b. turbidity;

c. extractability;

d. taste; and

e. pasteurization resistance.

In the following examples, designated 10-13, samples of the water-basedcoating compositions of Examples 1, 2, 4, and 9 (Examples 10-13 below)were applied to beverage container stock used to package beer and curedas indicated above. The cured sanitary liner compositions of theinvention were then evaluated to determine their effectiveness in theabove tests. Results are shown below.

                  EXAMPLES 10-13                                                  ______________________________________                                                    EXAMPLE                                                           ______________________________________                                                    10     11       12       13                                       ______________________________________                                        Formulation   Ex. 1    Ex. 2    Ex. 4  Ex. 9                                  Type Test and Result:                                                         ______________________________________                                        Metal adhesion                                                                              P        P        P      P                                      Turbidity     P        P        P      P                                      Extractability                                                                              P        P        P      P                                      Taste         P        P        P      P                                      Pasteurization resistance                                                                   P        P        P      P                                      ______________________________________                                         P = Passed.                                                              

As can be seen from the above, the compositions of this invention passedall of the important tests for sanitary liners.

It should be observed that a composition similar in formulation toExample 1, except that it contained 2.5 percent mercaptoethanol chaintransfer agent, failed to pass the taste test.

Definitions of the tests used in the above examples are as follows:

Metal Adhesion - The cured liner is tested for adhesion both prior toand after being in contact with the beer. The adhesion test employed isthe standard crosshatch adhesion test wherein the scribe lines are cutthrough the cured film to the substrate below, pressure-sensitiveadhesive tape is applied to the film and lifting of the film isattempted. The test is performed on both the original cured liner andthe liner after being immersed in beer under pasteurization conditions.In order to pass the test, the film must not lift from the substrate.

Turbidity - This test is performed by packing beer in a container coatedwith the sanitary liner and storing the container for periods of up toone month. In order to pass the test, the beer must not show anyturbidity after storage for 1 month.

Extractability - This test is conducted to ascertain whether the coatingcompositions meets FDA (Food and Drug Administration) guidelines and isperformed by applying the coating composition to metal foil and thencuring. The foil is then immersed in various extractants at 150° F. for2 hours and 120° F. until equilibrium (72 hours). The extractantsolutions are water, 8 percent ethanol in water, 3 percent acetic acidin water, and heptane. The extractant solutions are dried and residuesrecorded. The residues are reported as milligrams per square inch(mg./in.²) of coating.

Taste - This test measures the influence of cured coatings on beertaste. The test is performed by packing beer in containers containingthe cured liner and then storing the beer for various time periods(e.g., 1-6 months) at periodic intervals subjecting the beer to a tastepanel for evaluation.

A control, which is a packed beer container having a vinyl coating isoften employed. Members of the beer panel evaluate the beer forbitterness, acid taste, and the like. In order to pass the test,approval of the panel is required.

Pasteurization Resistance - The pasteurization resistance is determinedby immersing the cured liner in beer at a temperature of 160° F. for 30minutes. In order to pass the test, the film must show no blushing andadhesion must be unaffected. Adhesion is also checked during theevaluation by the standard cross hatch adhesion test. After immersion inbeer, pressure sensitive tape is applied to the film and lifting isattempted. To pass the test, the film must not lift from the substrate.

According to the provisions of the Patent Statutes, there are describedabove the invention and what are now considered to be its bestembodiments. However, within the scope of the appended claims, it is tobe understood that the invention can be practiced otherwise than asspecifically described.

We claim:
 1. A metal container containing a beverage and having itsinternal surface coated with an adherent sanitary liner, the coatingwhich is in contact with said beverage being a cured layer of awater-based coating composition consisting essentially of:A. from about5 percent to about 60 percent by weight of an amine-neutralized orpartially-neutralized interpolymer formed in the presence of a vinylpolymerization catalyst and in the absence of mercaptan, saidinterpolymer being comprised of:1. from about 5 percent to about 25percent of acrylamide or methacrylamide in units of the structure:##EQU2## where R' is methyl or hydrogen and R is hydrogen or lower alkylwith at least 50 percent of the groups represented by R being loweralkyl;
 2. 2. from about 3 percent to about 25 percent of units formed byvinyl polymerization of ethylenically unsaturated carboxylic acidselected from the group consisting of acrylic acid, methacrylic acid,itaconic acid, crotonic acid and maleic acid and half esters of maleicand fumaric acids;3. from about 5 percent to about 75 percent of unitsderived by vinyl polymerization of hardening monomer selected from thegroup consisting of styrene, vinyl toluene and alkyl methacrylateshaving 1 to 4 carbon atoms; and
 4. from about 5 percent to about 75percent of units formed by vinyl polymerization of flexibilizing monomerselected from the group consisting of alkyl acrylates having up to 13carbon atoms in each alkyl group and alkyl methacrylates having from 5to 16 carbon atoms in each alkyl group;wherein said interpolymer issolubilized by neutralizing or partially neutralizing the acid groups ofsaid interpolymer with a sufficient amount of monomeric amine to produceat least 0.200 milliequivalents of salt per gram of resin solids; and B.from about 40 percent to about 95 percent by weight of a liquid mediumconsisting of a mixture of water-soluble or water-miscible organicsolvents and water, wherein at least 60 percent by weight of the mixtureis water.
 2. The container of claim 1 wherein said beverage is selectedfrom the group consisting of beer, carbonated soft drinks,non-carbonated soft drinks, and fruit juice.
 3. A metal containercontaining a beverage and having its internal surface coated with anadherent sanitary liner, the coating which is in contact with saidbeverage being a cured layer of a water-based coating compositionconsisting essentially of:A. from about 15 percent to about 40 percentby weight of an amine-neutralized or partially-neutralized interpolymerformed in the presence of a vinyl polymerization catalyst and in theabsence of mercaptan, said interpolymer being comprised of:1. from about10 percent to about 15 percent of acrylamide or methacrylamide in unitsof the structure: ##STR2## where R' is methyl or hydrogen or R ishydrogen or lower alkyl with at least 50 percent of the groupsrepresented by R being lower alkyl;
 2. from about 5 percent to about 15percent of units formed by vinyl polymerization of ethylenicallyunsaturated carboxylic acid selected from the group consisting ofacrylic acid, methacrylic acid, itaconic acid, crotonic acid and maleicacid and half esters of maleic and fumaric acids;3. from about 40percent to about 60 percent of units derived by vinyl polymerization ofhardening monomer selected from the group consisting of styrene, vinyltoluene and alkyl methacrylates having 1 to 4 carbon atoms; and
 4. fromabout 20 percent to about 50 percent of units formed by vinylpolymerization of flexibilizing monomer selected from the groupconsisting of alkyl acrylates having up to 13 carbon atoms in each alkylgroup and alkyl methacrylates having 5 to 16 carbon atoms in each alkylgroup; wherein said interpolymer is solubilized by neutralizing orpartially-neutralizing the acid groups of said interpolymer with asufficient amount of monomeric amine to produce at least 0.200milliequivalents of salt per gram of resin solids; and B. from about 60to about 85 percent by weight of a liquid medium consisting of a mixtureof water-soluble or water-miscible organic solvents and water wherein atleast 60 percent by weight of the mixture is water.
 4. The container ofclaim 3 wherein said beverage is selected from the group consisting ofbeer, carbonated soft drinks, non-carbonated soft drinks, and fruitjuice.